Study Of Diffusion Influence Materials Of Copper-Zinc-Steel On The Hardness And Micro Hardness Under Heat Treatment

Ali Adwan H

doi:10.24237/djes.2019.12301

Authors

Ali Adwan H
aliadwanh@gmail.com
Department of Material Engineering, College of engineering, University of Diyala, Iraq

Keywords:

Heat treatments, re-crystallization, Micro Hardness, stainless steel

Abstract

Low melting metals like zinc used in this research to promote increasing of diffusion process with presence of pure powder of copper., this metals have good corrosion resistance in chemical and environmental conditions by making thin film to hardening surface of rod of stainless steel18/8Ni-Cr under heat treatment condition at 890c above eutectic line to reached austerity zone and under this line at ^0,600c to obtained re-crystallization annealing and 400c⁰at sufficient time 90min..chemical composition ,hardness ,micro-hardness ,and micro structures were investigated to track the effectiveness of diffusion zinc-copper melting in different s points.

Downloads

Download data is not yet available.

References

V.I. Bokshitskii, A.M. Glezer, E.K. Zakharov, G.A. SveshnikovaMetal Sci. Heat Treat. 39 (1997), pp. 38-41.

T.T. Sasaki, M. Barkey, G.B. Thompson, Y. Syarif, D. Fox.

Mater. Sci. Eng. A, B. Tuck, Atomic Diffusion in III-V Semiconductors (Hilger, Bristol, 1988), 528 (2011), pp. 2974-2981.

D. B. Darby, DPhil. Thesis, Oxford University, Department of Metallurgy and Science of Materials (1979).

A. G. Gad-Allah, M. M. Abou-Romia, M. W. Badawy and H. H. Rehan. Passivity of?-brass (Cu?Zn/67?33) and its breakdown in neutral and alkaline solutions containing halide ions. Journal of Applied Electrochemistry, (1991)21:9, 829-836.

T.M.H. Saber and A.A. El Warraky. (1993) Electrochemical and spectroscopic studies on dezincification of α-brass. Desalination 93:1-3, 473-486. Online publication date: 1-Aug-1993.

R.K. Dinnappa and S.M. Mayanna The dezincification of brass and its inhibition in acidic chloride and sulphate solutions. Corrosion Science 27:4, . (1987) 349-361. Online publication date: 1-Jan-1987.

L. Horner and E. Pliefke. (1986) Inhibitoren der Korrosion 31 (1). Beitrag zur Inhibierung der Korrosion von Zink und Messing. Materials and Corrosion/Werkstoffe und Korrosion37:8, 457-463.